GB 5310 12Cr2MoWVTiB high pressure seamless boiler tubes
GB 5310 12Cr2MoWVTiB high pressure seamless boiler tubes are designed and manufactured according to the Chinese national standard GB/T 5310-2017.
Please send your inquiry by sales@sunnysteel.com
Description
GB 5310 12Cr2MoWVTiB high pressure seamless boiler tubes are designed and manufactured according to the Chinese national standard GB/T 5310-2017.
GB 5310 12Cr2MoWVTiB high pressure seamless boiler tubes are a type of seamless steel tubes or pipes designed and manufactured according to the Chinese national standard GB/T 5310-2017. As stated in [1], they are made of pearlitic heat-resistant steel with a composition including Cr, Mo, W, V and Ti, which offer excellent high-temperature mechanical properties and corrosion resistance.
GB 5310 12Cr2MoWVTiB high pressure seamless boiler tubes are typically used in high-pressure boilers with working pressure above 9.8 MPa and working temperature between 450℃ and 650℃. They are mainly used for making superheaters, reheaters, steam pipes, and other high-pressure components in power plant boilers.
GB 5310 12Cr2MoWVTiB high-pressure seamless boiler tubes must meet strict standards for production and use, ensuring their safety and reliability in high-pressure applications. They come in various lengths, outer diameters, wall thicknesses, and end types such as plain end, beveled end, or threaded ends.
Application
12Cr2MoWVTiB boiler pipe is suitable for general structure, fluid transport, low and medium pressure boiler or boiling water piping, pipe size locomotive, petroleum, chemical, electric, power, high temperature, low temperature, corrosion, seamless refined plant, oil refining furnace, heat exchange tubes, fertilizer equipment, pipeline works etc.
12Cr2MoWVTiB steel is a kind of multi-element microalloyed low-alloy bainite heat-resistant steel developed by ourselves from the end of 1960s to the middle of 1970s in China. Due to the proper coordination of various alloy elements, the steel has high heat strength, and its heat strength performance and service temperature are higher than those of the same kind of steel abroad. Therefore, 12Cr2MoWVTiB can be used for boiler superheat tube panel and reheat The manufacture of boiler tube and main steam tube, in which superheater tube and reheater tube are called serpentine tube.
Temperature application range: wall temperature ≤ 600 ℃ (620 ℃ can be used when considering oxidation loss in strength calculation)
Chemical Compositions(%) of 12Cr2MoWVTiB
| Grade | C | Si | Mn | Cr | Mo | V |
| 12Cr2MoWVTiB | 0.08-0.15 | 0.45-0.75 | 0.45-0.65 | 1.60-2.10 | 0.50-0.65 | 0.28-0.42 |
| Ti | B | W | P | S | ||
| 0.08-0.18 | 0.002-0.008 | 0.30-0.55 | ≤0.025 | ≤0.015 |
Mechanical Properties of 20G
| Grade | Tensile strength(MPa) | Yield strength(MPa) | Elongation | Hardness |
| 12Cr2MoWVTiB | 540-735 | ≥345 | ≥18% | — |
The W.T. tolerance of 16Mn
| W.T.(S) | Tolerance of W.T. | |
| <3.5 | +15%(+0.48mm min) | |
| -10%(+0.32mm min) | ||
| 3.5-20 | +15%,-10% | |
| >20 | D<219 | ±10% |
| D≥219 | +12.5%,-10% | |
Process performance of 12Cr2MoWVTiB
(1) Forging:
The start temperature of rolling (forging) of 12Cr2MoWVTiB steel is 1150 ~ 1200ec, and the end temperature is 850 ° C. after rolling (forging), the steel is cooled by stacking.
(2) Cold bending
12Cr2MoWVTiB steel is mainly used for small-diameter steel tubes. Generally, the steel pipes need to be cold bent and do not need heat treatment after cold bending.
(3) Heat treatment process (according to GB5310-2008 standard)
Normalizing and tempering: normalizing temperature: 1020ec ~ 1060 ° C; holding for 30min; tempering temperature: 760ec ~ 790ec, holding for 3h; normalizing structure is granular bainite, normalizing + high temperature tempering structure is tempered bainite.
(4) Selection of welding materials:
The weldability of 12Cr2MoWVTiB steel is good. It can be used for manual arc welding, gas welding, friction welding, TIG welding and plasma welding. R347 welding rod is used for manual arc welding, h08cr2movnb welding wire is used for gas welding, butt joint with 12Cr1MoV steel, h08crmov or h08cr2movnb welding wire is used. Neutral partial oxidation flame is suitable for gas welding. After welding, it shall be normalized at 1000-1030 ℃ and tempered at 760-780 ° C. before manual arc welding with thickness greater than 6mm, it shall be preheated to 250-300ec, and tempered at 760-780 ° C after welding. After butt welding, it should be heated to 780ec, kept warm for 40 minutes, and then cooled to below 400ec.
Development of 12Cr2MoWVTiB high pressure boiler tube
◆Professor Liu rongzao put forward the theory of multiple composite strengthening in the 1960s, developed G102 (12Cr2MoWVTiB) in the late 1960s and G106 (10cr5mowvtib) in the 1970s
◆Professor Liu rongzao’s theory and G102’s success, Professor V.K. Sikka of the United States adores very much, and T91 research and development has been successful.
◆T23 (HCM2S, cc2199-3, 6cr2w2monbvnb) developed in Japan and T24 (cc2514, 6cr2mo1vtinb) developed in Europe are all G102 modifications.
In 1982, when Shanghai Boiler Plant and Harbin boiler plant introduced the manufacturing technology of 300MW and 600MW Subcritical controlled circulation boiler from CE company of the United States, CE company of the United States agreed to use 12Cr2MoWVTiB (steel 102) steel pipe instead of TP347H and TP304H steel tubes to manufacture 300MW and 600MW boiler high temperature superheater and reheater. In the superheater, the actual maximum design temperature of 102 steel tube is 580x ℃; in the reheater, the actual maximum design temperature of 102 steel pipe is 599 ℃.
According to DL / t715_, 12Cr2MoWVTiB steel is mainly used for superheater and reheater pipes with wall temperature not higher than 600 ° C; however, according to DL / T 715-2015, it is mainly used for superheater pipes and reheater pipes with wall temperature not higher than 575 ° C. It can be seen that the upper limit of service temperature in 2015 version is 25 ° C lower than that in 2000 version, which may be due to the serious oxidation problem when the steel is used in the steam side of the heating surface tube.
Other Name
- GB5310 12Cr2MoWVTiB boiler steel pipe
- 12Cr2MoWVTiB boiler pipe
- 12Cr2MoWVTiB pipe
Additional Condition
UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.
GB steel pipe execution standard
According to incomplete statistics, there are more than 240 national standard steel pipe production enterprises and more than 250 seamless steel pipe units.
Structural pipe (GB / T8162-1999) is used for the mechanical structure and general structure of seamless pipes.
Seamless pipe for liquid distribution (GB / T8163-1999) is a general seamless pipe for the transport of water, oil, gas and other liquids.
Seamless pipe is used for supply or transportation of water, oil, gas and other liquids under the specification of seamless pipe (GB / T8163-1999).
Correctly cooled or cold-rolled seamless steel pipe (GB3639-83) is used for mechanical structure, hydraulic equipment, high precision and surface finish. Selecting machines that produce seamless precision tubes or hydraulic equipment, etc., can greatly save mechanical processing time, improve material utilization, while helping to improve product quality.
Seamless pipe (GB3639-83) is basically improved the product quality though reduce the mechanical processing time and improve the material standard and quality. But it requires that it should be properly made by cooled or cold rolled seamless steel pipe (GB3639-83).
Low and medium pressure boiler pressure pipes (GB3087-1999) are used for the production of various low and medium pressure steam pipes, boiler water pipes and boilers with superheated steam, chimneys, small chimneys and domes use high quality hot rolled steel structures and cold drawn (laminated) seamless pipes.
Low and medium pressure boiler pressure pipe (GB3087-1999) is specialised for making of various low and medium pressure steam pipes, boiler water pipes and boilers with superheated steam, chimneys, and small chimneys.
High-pressure steam boiler pipe (GB5310-1995) is used for the production of high pressure and on the boiler surface pressure of hot water pipes made of high quality carbon steel, alloy steel and steel rust-free. (Working pressure is greater than 9.8Mpa, working temperature 540-650 degrees Celsius)
High quality carbon steel, alloy steel and steels are always required high pressure steam boiler pipe (GB5310-1995) for transportation and holding for liquid, steam, etc.
Pipeline for geological drilling (YB235-70) is a steel pipe for core drilling. It can be divided into drill pipe, neck drill, core tube, shell tube and sediment.
Core drilling is done though geological drilling (YB235-70) steel pipe and it’s segregated into drill pipe, neck drill, core tube, shell tube and sediment.
Piping (GB / T9711.1) is the supply of natural gas and other liquids such as oil and other seamless steel pipes (such as underground pipes and low temperature pipes).
High Pressure Cylinder Tube (GB18248) is used to produce oxygen cylinders, cylinder cylinders, natural gas cylinders, energy cylinders and other gas cylinders for seamless steel tubes.
Seamless steel pipe (GB / T9711.1) is used for the transporting and supplying of natural gas and other liquids such as oil.
Oxygen cylinders, cylinder cylinders, natural gas cylinders, energy cylinders and other gas cylinders is built by the High Pressure Cylinder Tube (GB18248) for seamless steel tubes.
Half-shaft automobile with seamless pipe (GB3088-82) is the manufacture of automobile tires and axles made of high-quality carbon structural steel and alloy steel pipes that melt the alloy structure.
Seamless pipe can be used in manufacturing of automobile tire and most of essential component of automobile industries. This specification consider under the standard of Half-shaft automobile with seamless pipe (GB3088-82).
Seamless steel pipe for ships (GB5213-85) is the production of grade I pressure piping, pressure pipe systems, boilers and seamless steel pipe coils. Carbon steel seamless pipe temperature does not exceed 450 ℃, seamless steel alloy steel pipe temperature of more than 450 ℃.
If the carbon steel pipe temperature does not exceed 450 ℃, it can be used for the production of grade I pressure piping and it consider under the standard of Seamless steel pipe for ships (GB5213-85)
Stainless steel structural stainless steel (GB / T14975-1994) is widely used in the fields of chemicals, petroleum, textiles, medical, food, machinery and other industries. Welded pipe and structural parts and parts made of hot stamping stainless steel, squeeze and seamless tubes.
Stainless steel structural steel (GB / T14975-1994) is used for the purpose of chemicals, petroleum, textiles, medical, food, machinery and other essential purpose works in different industries. Stainless tube considers all the function of squeeze and moulding with help of welded pipes and structural parts.
Stainless steel pipe for liquid distribution (GB / T14976-1994) is a seamless (extruded) and cold (laminated) seamless pipe made of stainless steel to transport liquids.
Liquid transportation is highly appreciated by the use of stainless steel pipe (GB / T14976-1994) but it is mandatory that seamless steel is cold laminated.
High pressure hose for chemical fertilizer equipment (GB6479-2000) suitable for working temperature -40 – 400 ℃, working pressure of chemical equipment 10 – 30Ma and carbon steel structural pipe High-grade seamless steel and alloy tubes.
Chemical fertilizer equipment (GB6479-2000) is used for the high pressure hose and it suits under the temperature of -40 – 400 ℃, working pressure of chemical equipment 10 – 30Ma and carbon steel structural pipe High-grade seamless steel and alloy tubes.
Uncured Pipes for Cracking Petroleum (GB9948-88) is a furnace tube, heat exchanger and seamless pipe for refineries.
Drill Diamond Core Drill (GB3423-82) is used for drilling diamond core drill, core rod, seamless pipe.
Seamless pipe drill diamond core drill (GB3423-82) is used for the drilling of diamond.
Oil Drill Tubing (YB528-65) is a seamless tube that thickens or thickens at both oil drills. The steel pipe is divided into two types of wire and wireless, and the wire is connected to the joint.
Diesel engine with high pressure pipe (GB3093-86) is the production of diesel injection system for high pressure pipe with no welded pipe.
Diesel engine with high pressure pipe (GB3093-86) is used for the production of diesel injection system for high pressure pipe, it doesn’t required welded pipe.
The internal precision pipe for hydraulic and pneumatic cylinders (GB8713-88) is a precision seamless pipe that is cold-rolled or cold-rolled with an accurate inner diameter for the production of hydraulic cylinders. and pneumatic. Columns, columns, can also be used for other cylinders and columns.
The production of hydraulic cylinders and pneumatic Columns, Columns these products require proper precision seamless pipe and the pipe should be cold- rolled or cold –rolled with an accurate inner diameter.
GB steel pipe size and tolerance
| Deviation level | Standardized outer diameter tolerance |
|---|---|
| D1 | ±1.5%，min ±0.75 mm |
| D2 | ±1.0%。min ±0.50 mm |
| D3 | ±0.75%．min±0.30 mm |
| D4 | ±0.50%。min ±0.10 mm |
| Process | Size(mm) | Tolerance | |
|---|---|---|---|
| Hot-rolled | O.D. | <351 | +/-1.0% D(+/-0.50min) |
| >=351 | +/-1.25% D | ||
| W.T. | <=25 | +/-12.5% S(+/-0.40 min) | |
| Cold drawn | O.D. | <=30 | +/-0.20 |
| 30-50 | +/-0.30 | ||
| >50 | +/-0.75% D | ||
| W.T. | <=3 | +12.5% S, -10% S | |
| >3 | +/-10% S | ||
Standard
The production of our seamless pipes is tightly regulated and all of the pipes we stock have been fully tested to international standards to ensure we only supply the highest quality products.
ASTM / ASME
American Society for Testing and Materials(ASTM), American Society of Mechanical Engineers (ASME)| Product name | Executive standard | Dimension (mm) | Steel code/ Steel grade |
|---|---|---|---|
| Black and Hot-dipped Zinc-coated Steel Pipes Seamless | ASTM A53 | 0.3-1200 x 1.0-150 | GR.A, GR.B, GR.C |
| Seamless Carbon Steel for High Temperature Service | ASTM A106 | 10.3-1200 x 1.0-150 | GR.B, GR.C |
| Seamless Cold-drawn Low-Carbon Steel Heat-Exchanger and Condenser Tubes | ASTM A179 | 10.3-426 x 1.0-36 | Low Carbon Steel |
| Seamless Carbon Steel Boiler Tubes for High Pressure | ASTM A192 | 10.3-426 x 1.0-36 | Low Carbon Steel |
| Seamless Cold-drawn Intermediate Alloy Steel Heat-exchanger and Condenser Tubes | ASTM A199 | 10.3-426 x 1.0-36 | T5, T22 |
| Seamless Medium-carbon Steel Boiler and Superheater Tubes | ASTM A210 | 10.3-426 x 1.0-36 | A1, C |
| Seamless Ferritic and Austenitic Alloy Steel Boiler, Superheater and Heat-exchanger Tubes | ASTM A213 | 10.3-426 x 1.0-36 | T5, T5b, T9 , T11, T22 ,T91 |
| Seamless Carbon and Alloy Steel for Mechanical Tubing | ASTM A333 | 1/4"-42" x SCH20-XXS | Grade1 Gr. 3,Gr..6, Gr.8 , Gr. 9 |
| Seamless Cold-drawn Carbon Steel Feedwater Heater Tubes | ASTM A556 | 10.3-426 x 1.0-36 | A2, B2 |
| Round and shaped steel cold formed welded and seamless carbon steel structural pipe. | ASTM A500 | OD :10.3-820 x 0.8- 75 | Grade A, B, C, D |
| Carbon and alloy steel mechanical tubing, either hot-finished or cold-finished | ASTM A519 | 10.3-426 x 1.0-36 | 1020, 1025, 4130, 4140 |
| For seamless ferritic alloy-steel pipe for high-temperature service | ASTM A335 | 1/4"-42" x SCH20-XXS | A/SA 335 P1, P2, P11, P12, P15, P22, P91, P92, P122 |
Process
Cold drawn seamless steel tube deformed process
Cold Drawn Seamless Mechanical Tubing (CDS) is a cold drawn 1018/1026 steel tube which offers uniform tolerances, enhanced machinability and increased strength and tolerances compared to hot-rolled products. 
Cold drawn steel tube is with hot-rolled steel coil as raw material, and tandem cold rolling pickled to remove oxide scale, its finished rolling hard roll, rolling hard volumes due to the continuous cold deformation caused by cold hardening strength, hardness increased indicators declined tough plastic, stamping performance will deteriorate, which can only be used for simple deformation of the parts. Rolling hard roll can be used as the raw material of the hot-dip galvanizing plant, hot dip galvanizing line set annealing line. Rolling hard roll weight is generally 6 to 13.5 tons, the coil diameter of 610mm.
Hot rolled seamless steel pipe deformed process
Hot-rolled seamless steel pipe production base deformation process can be summarized as three stages: perforation, extension and finishing. 
The main purpose of the perforation process is to become a solid round billet piercing hollow shell. Capillary in the specifications, accuracy and surface quality can not meet the requirements of the finished product, further improvements are needed to deform the metal through. The main purpose of the stretching machine is further reduced sectional view (main compression wall) for a larger axial extension, so that the capillary improved dimensional accuracy, surface quality and organizational performance. After stretching machine rolled steel pipe shortage collectively need further molding mill in order to achieve the requirements of the finished pipe. Rolled steel due to pass in the method widely used in the production of seamless steel tubes. So far, due to the method pass rolling steel can be divided into two categories: core pension without rolling rolling (hollow body rolling), and with the mandrel. Sizing machines, reducing mill and stretch reducing mill belonging to the hole without mandrel type continuous rolling mills are generally coffin. Its main purpose is to reduce the diameter of the deformation process or sizing get finished steel, the wall thickness of process control, can make thinning, thickening or nearly unchanged. All the traditional hole-type rolling machine with mandrel belong to extend machine. The main purpose is to reduce the deformation process perforated capillary wall thickness and outer diameter roll passes in the deformation zone and the mandrel posed, for a larger axial extension. At the same time a certain improvement in the organization, performance, accuracy, surface quality.
Cut to Length
Before cutting pipe and tubing No matter the material, measure the diameter of the pipe or tube to be cut to ensure that you use the right-size tube cutter for the job. When determining how to make a straight cut, use a tape measure and a pencil or other writing instrument to mark on the surface where you want to cut. If possible, mark around the circumference of a pipe, especially when cutting with a handsaw. Ensure that a cut is as straight as possible by securing the pipe with a vise, clamp, miter box or even duct tape to keep the length from shifting out of place while cutting. After cutting pipe and tubing
- Unless a cut is perfectly clean, you should expect to remove burrs from around the edge, especially after sawing.
- Use a deburring tool to clean the edge after tube cutting.
- You may opt to use a metal file on the cut of a metal pipe.
Inspection
Size inspection
Geometrical inspection of steel pipes The outer diameter, wall thickness, bending and length of the steel pipe can be inspected on the inspection table with an outer caliper, a micrometer and a bending ruler, and a length tape measure.
Tolerances of pipes you should notice
Take seamless steel pipe as an example, there are some tolerances that affect quality. Noting this, and you will get a better pipe.
Weight tolerance
For pipe NPS 12 (DN300, 323.8mm) and under, the weight shall vary within -3.5% / +10%.
For pipe over NPS 12 (DN300, 323.8mm), the weight shall vary within -5% / +10%.
Pipe of NPS 4 (DN100, 114.3mm) and smaller may be weighed in convenient lots; pipe in sizes larger than NPS 4 shall be weighed separately.
Quantity tolerance
Normally mills take -10% to +10% tolerance, but TPMCSTEEL keeps ±3% variation.
Length tolerance
For Seamless pipe& tube, if definite cut lengths are ordered, the length shall vary within -0mm / +6mm.
Dimension tolerances of seamless steel pipe
| Pipe types | Pipe Szie(mm) | Tolerances | |
|---|---|---|---|
| Hot rolled | OD | <50 | ±0.50mm |
| ≥50 | ±1% | ||
| WT | <4 | ±12.5% | |
| ≥4-20 | +15%, -12.5% | ||
| >20 | ±12.5% | ||
| Cold drawn | OD | 6-10 | ±0.20mm |
| 10-30 | ±0.40mm | ||
| 30-50 | ±0.45 | ||
| >50 | ±1% | ||
| WT | <1 | ±0.15mm | |
| >1-3 | + 15%, – 10% | ||
| >3 | + 12.5%, – 10% | ||
| Standard | Hot finished seamless tube | Cold flnished seamless tube | ||
|---|---|---|---|---|
| Out diameter (mm) | Tolerance | Out diameter (mm) | Tolerance | |
| EN10216-1 | ≤100 | +/-0.75% (min.+/-0.5mm) | All | +/-0.5% |
| EN10216-2 | (min. +/-0.30mm) | |||
| DIN17175 | >100 | +/-0.90% | ||
| GB/T 3087 | ≤460 | +/-0.75% (min.+/-0.5mm) | 10-30 | +/-0.40mm |
| >30-50 | +/-0.45mm | |||
| >50 | +/-1.0% | |||
| GB/T 5310 GB/T 9948 GB/T 6479 | <57 | +/-0.40mm | ≤30 | +/-0.20mm |
| 57-325 | +/-0.75% | >30-50 | +/-0.30mm | |
| >325-460 | +1%,-2mm | >50 | +/-0.8% | |
| ASME SA-179M ASME SA-192M ASME SA-209M ASME SA-210M ASME SA-213M JIS G 3461 JIS G 3461 | ≤101.6 | +0.4, -0.8mm | <25.4 | +/-0.10mm |
| >25.4-38.1 | +/-0.15mm | |||
| >38.1-50.8 | +/-0.20mm | |||
| 101.6-190.5 | +0.4, -1.2mm | >50.8-63.5 | +/-0.25mm | |
| >63.5-76.2 | +/-0.30mm | |||
| >76.2 | +/-0.38mm | |||
| ASME SA106 ASME SA335 | ≤48.3 | +/-0.40mm | ≤48.3 | +/-0.40mm |
| 48.3-114.3 | +/-0.79mm | |||
| 114.4-219.1 | +1.59, -0.79mm | |||
| 219.2-323.9 | +2.38, -0.79mm | >48.3 | +/-0.79mm | |
| >324 | +/-1.0% | |||
Tolerances on wall thickness
The wall thickness at any point shall be within the below tolerance table.| Standard | Hot finished seamless tube | Cold flnished seamless tube | ||||
|---|---|---|---|---|---|---|
| DIN17175 | Out diameter OD(mm) | Wall thickness T(mm) | Tolerance | Out diameter (mm) | Wall Thickness T(mm) | Tolerance |
| ≤130 | S≤2Sn | +15%, -10% | -- | All | +/-10% (min. +/-0.2mm) |
|
2Sn| +12.5%, -10% |
| |||||
| S>4Sn | +-/9% | |||||
| >130 | S≤0.05da | +17.5%, -12.5% | ||||
0.05da| +/-12.5% |
| |||||
| S>0.11da | +/-10% | |||||
| EN 10216-1 EN 10216-2 | ≤219.1 | - | +/-12.5% (min.+/-0.4mm) |
|||
| -- | T/D≤0.025 | +/-20% | ||||
0.025| +/-15% |
| |||||
0.05| +/-12.5% |
| |||||
0.1| +/-10% |
| |||||
| GB/T 3087 | -- | ≤20 | +15%,-12.5% (min.+0.45, -0.35mm) | -- | 1.0-3.0 | +15%, -10% |
| >20 | +/-12.5% | -- | >3 | +12.5%, -10% | ||
| GB/T 5310 GB/T 9948 GB/T 6479 | -- | <4.0 | +15%,-10% (min.+0.48, -0.32mm) | -- | 2-3 | +12%,-10% |
| 4-20 | +12.5%,-10% | >3 | +/-10% | |||
| >20 | +/-10% | |||||
| ASME SA-179M ASME SA-192M ASME SA-209M ASME SA-210M ASME SA-231M JIS G 3461 JIS G 3462 | -- | 2.41-3.8 | +35%, -0% | ≤38.1 | -- | +20%,-0% |
| 3.8-4.6 | +33%,-0% | >38.1 | -- | 22%,-0% | ||
| >4.6 | +28%,-0% | -- | -- | -- | ||
| ASME SA-106 ASME SA-335 | -- | All | +/12.5% | All | +/-10% | |
Note:
- The size in the table above is for the hot-rolled tubes.
- The size of the green area is the regular specification, we can accept orders directly, but the yellow area shall be subject to a technical evaluation.
- The Out side diameter (O.D) and wall thickness (W.T.) of the tube should be complied.
PMI test
Positive material identification (PMI) testing is the examination of a material, usually a metallic alloy, to confirm the material is consistent with the user’s request.
Delivery
Steel pipe delivery status(condition)
Steel pipe delivery status(condition): cold / hard (BK), cold / soft (BKW), after cold stress relief annealing (BKS), annealing (GBK), normalized (NBK).
Condition on delivery of steel pipe
| Term | Symbol | Explanation |
|---|---|---|
| Cold-finished/hard (cold-finished as-drawn) | BK | No heat treatment after the last cold-forming process. The tubes therefore have only low deformability. |
| Cold-finished/soft (lightly cold-worked) | BKW | After the last heat treatment there is a light finishing pass (cold drawing) With proper subsequent processing, the tube can be cold-formed (e.g. bent, expanded) within certain limits. |
| Annealed | GBK | After the final cold-forming process the tubes are annealed in a controlled atmosphere or under vacuum. |
| Normalized | NBK | The tubes are annealed above the upper transformation point in a controlled atmosphere or under vacuum. |
Cold rolled steel coil substrate products deep processing of high value-added products. Such as electro-galvanized, hot dip galvanized, electro-galvanized fingerprint resistant, painted steel roll damping composite steel, PVC laminating steel plates, etc., so that the excellent quality of these products has a beautiful, high resistance to corrosion, has been widely used.
Cold rolled steel coil finishing after annealing, cut the head, tail, trimming, flattening, smooth, heavy volume, or longitudinal clipboard. Cold-rolled products are widely used in automobile manufacturing, household electrical appliances, instruments, switches, buildings, office furniture and other industries. Steel plate strapping package weight of 3 to 5 tons. Flat sub-volume typically 3 to 10 tons / volume. Coil diameter 6m.
Packing
There are probably hundreds of different methods for packing a pipe, and most of them have merit, but there are two principles that are vital for any method to work prevent rusting and Sea transportation security. 
- Plastic caps plugged at the two sides of pipe ends
- Should be avoided by the steel strapping and transport damage
- Bundled signs should be uniform and consistent
- The same bundle(batch) of steel pipe should be came from the same furnace.
- The steel pipe has the same furnace number, the same steel grade, the same specifications.
Our packing can meet any needs of the customers.
Inquiry
Need to inquire about our products? Fill out the form below and our staff will be in touch!
FAQ
Q: How long is your delivery time? A: The delivery time of customized products is generally 25 35 days, and non customized products are generally shipped within 24 hours after payment. Q: Do you provide samples? Is it free? A: If the value of the sample is low, we will provide it for free, but the freight needs to be paid by the customer. But for some high value samples, we need to charge a fee. Q: What are your payment terms? A: T/T 30% as the deposit,The balance payment is paid in full before shipment Q: What is the packaging and transportation form? A: Non steaming wooden box and iron frame packaging. Special packaging is available according to customer needs. The transportation is mainly by sea. Q: What is your minimum order quantity? A: There is no minimum order quantity requirement. Customized products are tailor made according to the drawings provided by the customer.